Tunable spin polarization and superconductivity in engineered oxide interfaces

A sketch of the novel spin-polarized q2DEG obtained by embedding a FM EuTiO3 between LaAlO3 and SrTiO3.

In the study published on Nature Materials it was realized a new kind of 2DEG that possesses, besides a superconducting ground state, a strong spin-polarization. The result was obtained by inserting two atomic layers of the antiferromagnetic and insulating compound EuTiO3 between LaAlO3 and SrTiO3. The resulting heterostructures shows at the same time a robust ferromagnetic transition at a Curie temperature of 8 K and a superconducting transition below 150 mK. Using a prototype field effect device, the researchers showed that the degree of spin-polarization and the superconductive critical temperature can be both controlled by the electron carrier density of the 2DEG. As a consequence, the system is characterized by a complex phase diagram superconductivity emerges from a ferromagnetic normal state. This result has important implication for the potentialities of these materials in the field of oxide electronics alternative, at least in some particular cases, to the traditional semiconducting silicon based technology and to the new emerging 2D-materials 2D of interest in spintronics.

Contact
Dr. Marco Salluzzo
Researcher
CNR SPIN - Napoli
Telephone: +39 081 676 100 318
E-mail: marco.salluzzo@spin.cnr.it
Original Publication
Tunable spin polarization and superconductivity in engineered oxide interfaces
D. Stornaiuolo, C. Cantoni, G. M. De Luca, R. Di Capua, E. Di. Gennaro, G. Ghiringhelli, B. Jouault, D. Marrè, D. Massarotti, F. Miletto Granozio, I. Pallecchi, C. Piamonteze, S. Rusponi, F. Tafuri, M. Salluzzo
Nat. Mater. 15, 278–283 (2016)
DOI: 10.1038/nmat4491